dc.description53 Halamanen_US
dc.description.abstractPenelitian ini berjudul analisis sifat mekanik campuran bubur kertas dengan serat tanaman suku palmae (arecacea). Mengingat banyaknya limbah pelepah kelapa sawit dan pinang, maka peneliti melakukan pemanfaatan limbah tersebut menjadi serat. Serat tersebut dapat dijadikan sebagai salah satu bahan pembuatan komposit dengan campuran bubur kertas sebagai bahan utamanya. Dengan melakukan pengujian dan analisis kekuatan mekanik pada bahan tersebut, agar diketahui kekuatan sifat mekaniknya yang nantinya dapat berpotensi diaplikasikan pada bahan pembuatan karton box. Pengujian tarik dilakukan pada bahan komposit campuran bubur kertas dengan serat tanaman kelapa sawit dan pinang. Untuk dilakukannya pengujian tarik maka dilakukan pembuatan spesimen pengujian tarik dengan menggunakan tujuh variable spesimen uji dengan bahan komposit campuran bubur kertas dengan serat pelepah kelapa sawit dan pinang, dengan komposisi 30:70, 50:50, dan 70:30 pada masing masing campuran setiap serat. Dengan tambahan satu variable spesimen campuran bubur kertas dengan serat mix yaitu serat pelepah kelapa sawit dan pinang komposisi 30:70. Pembuatan spesimen menggunakan pedoman pada standard ASTM 3039M. Pengujian tarik dilakukan dengan menggunkan tensile test machine dilakukan pada fakultas pancasarjana universitas sumatera utara. Hasil pengujian dilakukan analisis dengan menggunakan metode offset. Dari hasil analisis diperoleh nilai tegangan tarik tertinggi terdapat pada spesimen, campuran bubur kertas dengan serat mix komposisi 30:70 dengan nilai 3,058 MPa. Regangan patah tertinggi terdapat pada spesimen campuran bubur kertas dengan serat pelepah pinang komposisi 30:70, dengan nilai regangan tarik 0,0267. Kekuatan luluh tertinggi terdapat juga pada spesimen campuran bubur kertas dengan serat pelepah pinang komposisi 30:70 dengan nilai 0,015 MPa. Modulus elastisitas tertinggi terdapat pada spesimen campuran serat pelepah kelapa sawit pada komposisi 30:70 dengan nilai 1,9107 MPa. The title of this research is the analysis of the mechanical properties of the mixture of pulp and plant fibers from the palmae (Arecacea) tribe. Considering the large amount of waste from oil palm and areca fronds, the researchers made use of the waste into fiber. These fibers can be used as a composite material with a mixture of pulp as the main ingredient. By testing and analyzing the mechanical strength of the material, it is necessary to know the strength of its mechanical properties which can then be potentially applied to the material for making cardboard boxes. Tensile testing was carried out on a composite material mixed with pulp with oil palm and areca nut plant fibers. To carry out the tensile test, a tensile test specimen was made using seven test specimen variables with a composite material of a mixture of pulp with palm midrib and areca nut fibers, with a composition of 30:70, 50:50, and 70:30 in each mixture of each fiber. . With the addition of one variable specimen of pulp mixed with mixed fiber, namely palm midrib fiber and areca nut with a composition of 30:70. Making specimens using the guidelines on the ASTM 3039M standard. Tensile testing was carried out using a tensile test machine at the Pancasarjana faculty of the University of North Sumatra. The test results were analyzed using the offset method. From the results of the analysis, the highest tensile stress value was found in the specimen, a mixture of pulp and fiber mix composition of 30:70 with a value of 3,058 MPa. The highest fracture strain was found in the mixed pulp specimen with betel nut fiber composition 30:70, with a tensile strain value of 0.0267. The highest yield strength was also found in specimens of mixed pulp with betel nut fiber composition 30:70 with a value of 0.015 MPa. The highest modulus of elasticity was found in the mixed specimen of oil palm midrib fiber at a composition of 30:70 with a value of 1.9107 MPa.en_US
dc.language.isoiden_US
dc.publisherUniversitas Medan Areaen_US
dc.relation.ispartofseriesNPM;198130143-
dc.subjectbubur kertasen_US
dc.subjectserat pelepah kelapa sawiten_US
dc.subjectserat pelepah pinangen_US
dc.subjectuji tariken_US
dc.subjectpaper pulpen_US
dc.subjectoil palm midrib fiberen_US
dc.subjectareca palm fiberen_US
dc.subjecttensile testen_US
dc.titleAnalisis Sifat Mekanik Campuran Bubur Kertas Dengan Serat Tanaman Suku Palmae (Arecaceae)en_US
dc.title.alternativeAnalysis of Mechanical Properties of Pulp Mix with Palmae (Arecaceae) Plant Fibersen_US
dc.typeThesisen_US
Appears in Collections:SP - Mechanical Engineering

Files in This Item:
File Description SizeFormat 
198130143 - Nazaruddin Yusman - Fulltext.pdfCover, Abstract, Chapter I, II, III, V, Bibliography1.11 MBAdobe PDFView/Open
198130143 - Nazaruddin Yusman - Chapter IV.pdf
  Restricted Access
Chapter IV536.12 kBAdobe PDFView/Open Request a copy


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.